原包三菱低氣味高抗沖POM Iupital FU2010R2
|
Density |
1.38 |
g/cm? |
ISO 1183 |
|
Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) |
6.0 |
cm?/10min |
ISO 1133 |
| Mechanical |
Nominal Value |
Unit |
Test Method |
|
Tensile Stress (Yield) |
51.0 |
MPa |
ISO 527-2/50 |
|
Tensile Strain |
|
|
ISO 527-2/50 |
|
Yield |
10 |
% |
|
|
Break |
50 |
% |
|
|
Flexural Modulus 3 |
2000 |
MPa |
ISO 178 |
|
Flexural Stress 3 |
70.0 |
MPa |
ISO 178 |
| Impact |
Nominal Value |
Unit |
Test Method |
|
Charpy Notched Impact Strength (23°C) |
9.0 |
kJ/m? |
ISO 179 |
|
Charpy Unnotched Impact Strength (23°C) |
No Break |
|
ISO 179 |
| Thermal |
Nominal Value |
Unit |
Test Method |
|
Heat Deflection Temperature (1.8 MPa, Unannealed) |
87.0 |
°C |
ISO 75-2/A |
|
Melting Temperature |
166 |
°C |
ISO 11357-3 |
| Flammability |
Nominal Value |
|
Test Method |
|
Flame Rating (0.8 mm) |
HB |
|
UL 94 |
用途
多聚甲醛為高甲醛含量的固態(tài)甲醛，呈固體顆粒狀、便于貯存和運(yùn)輸。在較高的溫度下能變成甲醛蒸氣，易于代替高濃度甲醛參與各種反應(yīng)，有利于化工、制藥等化學(xué)合成及其他工業(yè)領(lǐng)域的應(yīng)用，特別是在要求使用無水甲醛作原料的合成方面，用途***。主要有以下幾方面（1）農(nóng)藥：合成乙草胺、丁草胺和草甘膦等；（2）涂料：合成***汽車用漆；（3）樹脂：合成脲醛樹脂、酚醛樹脂、聚縮醛樹脂、蜜胺樹脂、離子交換樹脂等及各種粘合劑；（4）造紙：合成紙張?jiān)鰪?qiáng)劑； （5）鑄造：翻砂脫膜劑、合成鑄造粘合劑；（6）養(yǎng)殖業(yè)：薰蒸消毒劑。（7）有機(jī)原料：用于制備季 戊 四 醇、三羥甲基丙烷、甘油、丙烯酸、丙烯酸甲酯、甲基丙烯酸、N－羥基甲基丙烯酰胺、烷基苯酚、甲基乙烯基酮等。（8）其他：醫(yī)藥及消毒。